| Type | Transparent SLA Resin |
| Color | Clear |
| Density | 1.11 - 1.14g/cm³ @ 25 ℃ |
| Viscosity | 325 - 425 cps @ 28 ℃ |
| Dp Value | 0.135 - 0.155 mm |
| Ec Value | 9 - 12 mJ/c㎡ |
| Layer Thickness | 0.1 - 0.15 mm |
| Shore Hardness | 72 - 78 D |
| Flexural Modulus | 2,680 - 2,775 MPa |
| Flexural Strength | 65 - 75 MPa |
| Tensile Modulus | 2,170 - 2,385 MPa |
| Tensile Strength | 25 - 30 MPa |
| Elongation at Break | 12 - 20 % |
| Impact Strength | 58 - 70 J/m |
| Heat Deflection Temperature (HDT) | 50 - 60 °C |
| Glass Transition Temperature (Tg) | 55 - 70 °C |
Transparent SLA Resin with High Clarity
Art & Design 
Automotive Industry 
Consumer Goods 
Rapid Prototyping KS158T is a transparent SLA resin with high strength and precise detail reproduction. Due to its clarity, it is ideal for applications where optical transparency or light transmission is crucial — such as design prototypes, lens molds, or fluidic components. The mechanical properties are excellent, with tensile strength up to 60 MPa and outstanding flexural strength above 80 MPa.
Thanks to its smooth, clear surface, the parts can be easily post-processed — for example, by polishing or painting. However, the relatively low heat deflection temperature (HDT) of 52 °C limits its thermal use range, so it is primarily recommended for functional prototypes and aesthetic parts.
Request a customized quote now.
Advantages
High light transmission
Ideal for transparent parts
High detail accuracy and fine finish
Typical Applications
Design prototypes
Transparent covers
Light guides
Aesthetic pattern parts