Type SLA Resin
Color Slightly yellow, transparent
Density 1.121 - 1.125 g/cm @ 25 °C
Viscosity 251 - 305 cps @ 27 °C
Dp 0.16 mm
Building layer thickness 0.05 - 0.125 mm
Hardness Shore D 83 - 85 D
Flexural modulus 2400 - 2800 MPa
Flexural strength 46 - 57 MPa
Tensile modulus 1300 - 1600 MPa
Tensile strength 30 - 37 MPa
Elongation at break 2.3 - 3.8 %
Impact strength notched Izod 12 - 20 J/m
Heat deflection temperature (HDT) 140 - 150 °C

UV Resin KS1208H

  • High temperature resistance – Sustained use at approx. 120 °C, short-term resistance above 200 °C
  • Excellent dimensional stability – Ideal for precise engineering parts
  • High strength and fine surface quality – Mechanically robust with detailed surface resolution
  • Low viscosity – Optimized for efficient SLA processing
  • Good impact strength – Suitable for functional prototypes and quick mold making
  • Rapid Prototyping
Data Sheet 3D Printer Contact

KS1208H is a high-temperature-resistant SLA resin with low viscosity and a slightly yellow transparent appearance. It is an excellent solution for parts requiring thermal durability and dimensional accuracy. Well-suited for functional prototypes, rapid mold production, and small-batch manufacturing under heat and humidity conditions.

Advantages

  • Thermal resistance up to 120 °C continuous

  • Short-term heat resistance above 200 °C

  • Excellent dimensional accuracy

  • Good mechanical properties

  • High surface detail resolution

Typical Applications:

  • High-temp resistant prototypes

  • Quick molds

  • Functional parts requiring accuracy

  • Small-batch production under thermal load