| Typ | Granulate |
| Density | 1.3 g/cm³ |
| Melt index (220 °C / 10 kg) | 197 g/10 min |
| Melt index (200°C / 5kg) | 65 g/10 min |
| Rockwell hardness r scale 23°C | 84 |
| Tensile Strength | 50.5 MPa |
| Young's Modulus | 4780 MPa |
| Elongation at at break | 9.6 % |
| Flexural Strength | 61 MPa |
| Flexural Modulus | 2234 MPa |
| IZOD Impact Notched | 48 J/m |
| Heat Deflection (HDT) | 54.5 °C |
| Glass Transition (Tg) | 58.8 °C |
| Melting Point | 162.6 °C |
| Vicat Softening Temperature | 54 °C |
| Mold Shrinkag | 0.1 - 0.3 % |
Art & Design 
Consumer Goods 
Furniture Industry P716-PLA is an eco-friendly PLA granulate (polylactic acid) derived from plant-based resources such as corn starch. It is biodegradable, features a glossy surface, high stiffness, and dimensional stability, while being easy to process.
This material is ideally suited for indoor applications such as furniture decorations, creative objects, art pieces, toys, and handmade products. With REACH compliance and UL certification, it’s also suitable for professional use. P716-PLA is a great balance between sustainability, aesthetics, and performance.
Typical Applications