| Type | Nylon Powder |
| Tensile Modulus | 3000 Mpa |
| Tensile Strength | 46 Mpa |
| Elongation at Brea | 9% |
| Charpy Impact Strength | 36 KJ/m² |
| Charpy Notched Impact Strength | 6 KJ/m² |
| Flexural Modulus | 2800 Mpa |
| Flexural Strength | 70 Mpa |
| Melting Temperature (10°C/min) | 187 °C |
| Vicat Softening Temperature (50°C/h, 50N) | 150 °C |
| Density (Laser Sintered) | 1.2 g/cm³ |
| Density (Powder) | 0.72 g/cm³ |
| Particle Size (D50) | 50 μm |
Aerospace 
Automotive Industry 
Electronics & Electrical Engineering 
Mechanical Engineering 
Rapid Prototyping 
Small Batch Production KSPA12GB is a high-performance technical material for Selective Laser Sintering (SLS), based on nylon and reinforced with 30% glass beads. This results in printed parts with excellent mechanical stiffness, high heat resistance, and outstanding dimensional stability.
With its near 100% powder reuse rate, KSPA12GB offers both economic and environmental advantages in additive manufacturing workflows. Its smooth, blue-gray finish makes it ideal for functional prototypes, structural parts, and end-use components in automotive, aerospace, architecture, and electronics sectors.
Request your customized quote now.
Typical Applications