| Type | Nylon Powder |
| Tensile Modulus | 1600 Mpa |
| Tensile Strength | 46 Mpa |
| Elongation at Break | 20% |
| Charpy Impact Strength | 38 KJ/m² |
| Charpy Notched Impact Strength | 7.5 KJ/m² |
| Flexural Modulus | 1400 Mpa |
| Flexural Strength | 50 Mpa |
| Melting Temperature (10°C/min) | 187 °C |
| Vicat Softening Temperature (50°C/h 50N) | 100 °C |
| Density (Laser Sintered) | 0.94 g/cm³ |
| Density (Powder) | 0.52 g/cm³ |
| Particle Size (D50) | 50 μm |
Aerospace 
Architecture & Construction 
Automotive Industry 
Consumer Goods 
Electronics & Electrical Engineering 
Mechanical Engineering 
Rapid Prototyping 
Small Batch Production KSPA12ST is a white nylon powder with a D50 particle size of approx. 50 μm, specially designed for Selective Laser Sintering (SLS). The powder exhibits high sphericity, exceptional flowability, and uniform size distribution. Developed using Kings’ in-house synthesis technology, it combines cost efficiency with excellent surface finish and reliable mechanical properties.
Even when reused close to 100%, KSPA12ST maintains outstanding print quality and mechanical strength. It is ideal for applications in aerospace, automotive, architecture, and electronics.
KSPA12 is the ideal choice for engineers, designers, and manufacturers who value reliability, versatility, and cost-efficiency in the SLS printing process.
Typical Applications